Análisis del comportamiento mecánico de los suelos limo arenosos, estabilizado con cal y cemento

Autores/as

  • Castro-Solís Arnaldo Andreé Maestría en Ingeniería Civil, Mención Vialidad, Instituto de Posgrado, Universidad Técnica de Manabí. Portoviejo, Ecuador. https://orcid.org/0009-0008-0920-0400
  • Ortiz-Hernández Eduardo Departamento de Construcciones Civiles y Arquitectura, Facultad de Ciencias Matemáticas, Físicas y Químicas, Universidad Técnica de Manabí. Portoviejo, Ecuador. https://orcid.org/0000-0002-1885-6005
  • Macías-Sánchez Lucia Departamento de Construcciones Civiles y Arquitectura, Facultad de Ciencias Matemáticas, Físicas y Químicas, Universidad Técnica de Manabí. Portoviejo, Ecuador. https://orcid.org/0000-0002-9921-4943

DOI:

https://doi.org/10.46296/ig.v7i13.0153

Palabras clave:

Suelo limo arenoso, cal, cemento, comportamiento mecánico del suelo

Resumen

En esta investigación de estabilización de los suelos limos arenosos con cal y cemento se determinó el comportamiento mecánico de estos que incluyeron la realización de ensayos de laboratorio como son: granulometría, ensayos de Límites de Atterberg, ensayo de Proctor, ensayo de capacidad portante (CBR), y ensayos de Permeabilidad. Con el fin de analizar cómo cambian las propiedades del material, además se compararon las propiedades del suelo limo - arenosos en estado natural y posteriormente adicionando la cal y el cemento en porcentajes de 3%, 6% y 9%. Se realizaron otros tipos de estudios dinámicos para explorar las propiedades del suelo, se adicionó el ensayo de permeabilidad de carga constante, utilizando los agentes incorporados de cal y cemento teniendo como resultado una baja permeabilidad con cal para el 3% con 2.65E-05 cm/s, con el 6% 5.12E-06 cm/s, posteriormente se realizó el ensayo de permeabilidad con el empleo de  cemento  teniendo como resultado con el 3% un 2.44E-06 cm/s, con el 6% con 2.58E-06 cm/s y con el 9% un 2.55E-07 cm/s.

Palabras clave: Suelo limo arenoso, cal, cemento, comportamiento mecánico del suelo.

Abstract

In this research on the stabilization of sandy loam soils with lime and cement, the mechanical behavior of these soils was determined, which included laboratory tests such as particle size analysis, Atterberg Limits tests, Proctor compaction test, California Bearing Ratio (CBR) test, and Permeability tests. In order to analyze how the properties of the material change, the properties of the sandy loam soil in its natural state were compared with those after adding lime and cement at percentages of 3%, 6%, and 9%. Other dynamic studies were conducted to explore soil properties, including the constant head permeability test. Lime was added as an admixture, resulting in low permeability with 3% lime at 2.65E-05 cm/s, and with 6% lime at 5.12E-06 cm/s. Subsequently, the permeability test was conducted using cement as an admixture, resulting in 3% cement at 2.44E-06 cm/s, 6% cement at 2.58E-06 cm/s, and 9% cement at 2.55E-07 cm/s.

Keywords: Sandy silt soil, lime, cement, mechanical behavior of the soil.

Información del manuscrito:
Fecha de recepción:
18 de octubre de 2023.
Fecha de aceptación: 19 de diciembre de 2023.
Fecha de publicación: 10 de enero de 2024.

Citas

Aiassa, G. M., & Arría, P. A. (2007). DISEÑO DE MEZCLAS DE SUELO COMPACTADO PARA LA CONSTRUCCIÓN DE TERRAPLENES. Revista EIA, 7, 51-61.

FAO. (2015). Agricultura Sostenible. Organización de Las Naciones Unidas Para La alimentación y La Agricultura FAO. http://www.fao.org/sustainable-development-goals/overview/fao-and-post-2015/sustainable-agriculture/es/

FAO. (2023). El suelo, diferencias según su aspecto físico y químico. https://www.fao.org/3/ah645s/AH645S04.htm

González, M., Moreno, C., & Egido, J. (2015). Influencia del manejo sobre la calidad del suelo. ECUADOR ES CALIDAD - Revista Científica Ecuatoriana, 2(1), 33–40.

Descargas

Publicado

2024-01-10

Cómo citar

Castro-Solís, A. A., Ortiz-Hernández, E., & Macías-Sánchez, L. (2024). Análisis del comportamiento mecánico de los suelos limo arenosos, estabilizado con cal y cemento. Revista Científica INGENIAR: Ingeniería, Tecnología E Investigación. ISSN: 2737-6249., 7(13), 69-79. https://doi.org/10.46296/ig.v7i13.0153