Análisis del comportamiento de juntas constructivas entre hormigones antiguos y hormigones nuevos empleando epóxicos estructurales

Resumen

La presente investigación estudia el comportamiento de juntas constructivas de hormigones de diferentes edades que fueron unidos con resina estructural mono componente a base de poliuretano con la finalidad de evaluar su comportamiento ante cargas. las muestras ensayadas fueron obtenidas de edificaciones que se encuentran dentro de la ciudad de Portoviejo de donde se extrajeron cilindros con edades mayores a los 8 años y otro inferior a los 8 meses, el objetivo de la investigación fue analizar el comportamiento de juntas constructivas entre hormigones de diferentes unidos con una resina estructural, con los testigos tomados se realizaron los ensayos para determinar la absorción posterior ensayados a tracción indirecta. En los ensayos de tracción indirecta se observaron valores máximos de 3.70 MPa y como mínimo de 2.02 MPa donde se observaron desprendimiento de secciones en los extremos de los cilindros, no se observaron daños que pudieran indicar una separación de los dos elementos unidos. Los ensayos de resistencia a la tracción indicaron que la resina monocapa presenta un buen comportamiento ante este tipo de ensayos y demuestra ser adecuada para unir hormigones de diferentes edades.

Palabras clave: Resina monocomponente, junta estructural, resistencia a la compresión, hormigones.

Abstract

The present investigation studies the behavior of construction joints of concrete of different ages that were joined with single-component structural resin based on polyurethane in order to evaluate their behavior under loads. the tested samples were obtained from buildings located within the city of Portoviejo from where cylinders older than 8 years and another younger than 8 months were extracted, the objective of the research was to analyze the behavior of constructive joints between concrete of different joints with a structural resin, with the witnesses taken the tests were carried out to determine the subsequent absorption tested at indirect traction. In the indirect traction tests, maximum values of 3.70 MPa and a minimum of 2.02 MPa were observed where detachment of sections at the ends of the cylinders were observed, no damage was observed that could indicate a separation of the two joined elements. The tensile strength tests indicated that the monolayer resin performs well in this type of test and proves to be suitable for bonding concrete of different ages.

Keywords: Monocomponent resin, structural joint, compressive strength, concrete.

Información del manuscrito:
Fecha de recepción: 06 de junio de 2022.
Fecha de aceptación: 19 de septiembre de 2022.
Fecha de publicación: 29 de septiembre de 2022.